Fe-based Nanocrystalline Core

High Initial Permeability Nanocrystalline Core

P/N: CP77-86-10A
ID=77mm, OD=86mm, H=10mm
Le: 25.6cm, Ac: 0.34cm2, Weight: 85g
AL value ≥19μH@1kHz/0.3V

P/N: CE100-125-10A
ID=100mm, OD=125mm, H=10mm (nominal)
Le: 35.33cm, Ac: 0.94cm2, weight: 258g
AL value ≥39μH@1kHz/0.3V/100Ω

Low Hysteresis Loss Nanocrystalline Core

P/N: CP90-120-20A
ID=90mm, OD=120mm, H=20mm
Le: 32.97cm, Ac: 2.25cm2, Weight: 678g
AL value ≥100μH@1kHz/0.3V
High grade soft magnetic cores with high permeability
Used for high precision current transformers

Epoxy Coated Nanocrystalline Core

P/N: CE60-68-30A
Compact size, good protection for direct winding
Adjustable Br/Bs ratio by annealing technicals and pre-treatment
ID=60mm, OD=68mm, H=30mm
Le: 20.1cm, Ac: 1.05cm², Weight: 129g
AL value ≥25.5μH@1kHz/0.25V

Nanocrystalline Ribbon Wound Core

P/N: CE20-25-25A
ID=20mm, OD=25mm, H=25mm
Le: 7.07cm, Ac: 0.469cm², Weight: 26.8g
AL value ≥48μH@1kHz/0.25V
Wound by very thin tape (spraying strip)
Suit for direct coil winding of current transformer

Good Temperature Stability Nanocrystalline Core

P/N: CP19-26-10A
ID=19mm, OD=26mm, H=10mm (nominal)
Le: 7.07cm, Ac: 0.26cm², Weight: 16.8g
AL value ≥54μH@1kHz/0.3V
Suit for 120A mini current transformer

Toroidal Nanocrystalline Core

P/N: CA60-100-30A
ID=60mm, OD=100mm, H=30mm (nominal)
Le: 25.12cm, Ac: 4.5cm2, weight: 977g
AL value ≥263μH@1kHz/0.3V