Fe-based Nanocrystalline Choke Core
Fe-based Nanocrystalline Choke Core

Fe-based Nanocrystalline Choke Core

Features

  • ID=32mm, OD=40mm, H=15mm (nominal)
  • Le:11.3cm, Ac: 0.45cm2, Weight: 52g
  • AL value ≥47.2μH@10kHz/0.1V/1Ts
  • 15mm 1k107 ribbon wound, fixed by sponge after annealing
  • Adjustable remanence due to different annealing technical

Specifications

Part NumberCP32-40-15A
DescriptionFe-based Nanocrystalline Choke Core
StructureToroidal
Material1k107 Nanocrystalline 15mm Ribbon
Finish TypeWhite PBT Plastic Box
Saturation Magnetic Induction (Bs)1.25 T
Crystallization Temperature (Tx)500 °C
Curie Temperature (Tc)570 °C
Density (ρ)7.20 g/cm3
Resistivity130 μΩ.cm
Filling Coefficient≥ 0.75
Mean Magnetic Path (Le)11.3 cm
Net Area (Ac)0.45 cm2
AL Value≥ 47.2 μH
Test Conditions10 kHz / 0.1 V / 1 Ts
WeightApprox. 52 g
Accept CustomizedYes

Dimensions

CP32-40-15A, Fe-based Nanocrystalline Choke Core
CP32-40-15A, Fe-based Nanocrystalline Choke Core
Dimensions (mm)IDODHT
Nominal Size32±0.540±0.515±0.2
Finish Size29±0.545±0.519±0.5