Low Hysteresis Loss Nanocrystalline Core
Low Hysteresis Loss Nanocrystalline Core

Low Hysteresis Loss Nanocrystalline Core

Features

  • ID=90mm, OD=120mm, H=20mm
  • Le: 32.97cm, Ac: 2.25cm2, Weight: 678g
  • AL value ≥100μH@1kHz/0.3V
  • High grade soft magnetic cores with high permeability
  • Used for high precision current transformers

Specifications

Part NumberCP90-120-20A
DescriptionLow Hysteresis Loss Nanocrystalline Core
StructureToroidal
MaterialFe-based 1k107 Nanocrystalline
Finish TypePBT Plastic Box
Saturation Magnetic Induction (Bs)1.25 T
Crystallization Temperature (Tx)500 °C
Curie Temperature (Tc)570 °C
Density (ρ)7.20 g/cm3
Resistivity130 μΩ.cm
Filling Coefficient≥ 0.75
Mean Magnetic Path (Le)32.97 cm
Net Area (Ac)2.25 cm2
AL Value≥ 100 μH
Test Conditions1 kHz / 0.3 V @ 1Ts
WeightApprox. 678 g
Accept CustomizedYes

Dimensions

CP90-120-20A, Low Hysteresis Loss Nanocrystalline Core
CP90-120-20A, Low Hysteresis Loss Nanocrystalline Core
Dimensions (mm)IDODH
Nominal Size90±0.5120±0.520±0.2
Finish Size84.9±0.3125.2±0.325.4±0.3