P/N: CP77-86-10A
ID=77mm, OD=86mm, H=10mm
Le: 25.6cm, Ac: 0.34cm2, Weight: 85g
AL value ≥19μH@1kHz/0.3V
High Initial Permeability Nanocrystalline Core
PCB Mount Nanocrystalline CM Choke Core
P/N: CP20-32-10B
ID=20mm, OD=32mm, H=10mm (bare core)
Le: 8.16cm, Ac: 0.45cm2, Weight: 29.9g
AL value ≥26.5μH@16kHz/1V
10mm 1k107 tape wound core fixed by silicon grease after annealing
Good mechanical protection by PBT box with rib & base
High Permeability Common Mode Choke Core
P/N: CP20-32-10A
ID=20mm, OD=32mm, H=10mm (nominal)
Le: 8.164cm, Ac: 0.45cm2, Weight: 31.8g
AL value ≥26.5μH@16kHz/1V
Permeability ≥80000 @ 1kHz, low iron loss
Low price & high saturation induction than permalloy cores
Epoxy Coat Nanocrystalline Choke Core
P/N: CE10.8-17.7-8A
ID=10.8mm, OD=17.7mm, H=8mm (nominal)
Le: 4.48cm, Ac: 0.209cm2, Weight: 8g
AL value ≥70μH@10kHz/4mA
8mm 1k107 thin type ribbon wound
Fe-based Nanocrystalline Choke Core
P/N: CP32-40-15A
ID=32mm, OD=40mm, H=15mm (nominal)
Le:11.3cm, Ac: 0.45cm2, Weight: 52g
AL value ≥47.2μH@10kHz/0.1V/1Ts
15mm 1k107 ribbon wound, fixed by sponge after annealing
Adjustable remanence due to different annealing technical
Nanocrystalline Ribbon Wound Core
P/N: CE20-25-25A
ID=20mm, OD=25mm, H=25mm
Le: 7.07cm, Ac: 0.469cm2, Weight: 26.8g
AL value ≥48μH@1kHz/0.25V
Wound by very thin tape (spraying strip)
Suit for direct coil winding of current transformer
Good Temperature Stability Nanocrystalline Core
P/N: CP19-26-10A
ID=19mm, OD=26mm, H=10mm (nominal)
Le: 7.07cm, Ac: 0.26cm2, Weight: 16.8g
AL value ≥54μH@1kHz/0.3V
Suit for 120A mini current transformer
Plastic Box Nanocrystalline Choke Core
P/N: CP16-26-10A
ID=16mm, OD=26mm, H=10mm (nominal)
Le: 6.59cm, Ac: 0.38cm2, Weight: 15g
AL value ≥26.5μH@16kHz/1V
10mm 1k107 ribbon wound, fixed by silicon grease after annealing
Good mechanical protection by PBT box with separator