P/N: CP100-140-40A
ID=100mm, OD=140mm, H=40mm (nominal)
Le: 37.68cm, Ac: 6.0cm2, Weight: 1670g
AL value ≥234μH@1kHz/0.3V
Stacked by 2 pieces 20mm tape-wound core
Power Distribution Nanocrystalline Core

P/N: CP100-140-40A
ID=100mm, OD=140mm, H=40mm (nominal)
Le: 37.68cm, Ac: 6.0cm2, Weight: 1670g
AL value ≥234μH@1kHz/0.3V
Stacked by 2 pieces 20mm tape-wound core
P/N: CP90-120-20A
ID=90mm, OD=120mm, H=20mm
Le: 32.97cm, Ac: 2.25cm2, Weight: 678g
AL value ≥100μH@1kHz/0.3V
High grade soft magnetic cores with high permeability
Used for high precision current transformers
P/N: CB80-115-25A
ID=80mm, OD=115mm, H=25mm (nominal)
Le: 30.62cm, Ac: 3.28cm2, Weight: 819g
AL value ≥157μH@1kHz/0.3V
High permeability, good termal stability, low core loss
Important parts for current transformers in power system
P/N: CRSR134-106-14-15A, CRSR94-76-14-16A, CRSR181-130-10-10A;
Weight: 620/459/350g, Le: 51.95/37.95/64.90cm, Ac: 1.68/1.79/0.9 cm2;
High permeability ribbon 15/16/10mm;
Narrow gap after cutting and grinding
P/N: CS110-145-20A
ID=110mm, OD=145mm, H=20mm (nominal)
Le: 40.04cm, Ac: 2.63cm2, weight: 1000g
AL value ≥96μH@1kHz/0.3V
Suit for metal clad or metal enclosed LV/MV switchgear
P/N: CA60-100-30A
ID=60mm, OD=100mm, H=30mm (nominal)
Le: 25.12cm, Ac: 4.5cm2, weight: 977g
AL value ≥263μH@1kHz/0.3V