P/N: CP40-50-20B
ID=40mm, OD=50mm, H=20mm
Le: 14.13cm, Ac: 0.75cm2, Weight: 93.5g
AL value ≥78μH@1kHz/0.3V
Wide Frequency Nanocrystalline CMC Core

P/N: CP40-50-20B
ID=40mm, OD=50mm, H=20mm
Le: 14.13cm, Ac: 0.75cm2, Weight: 93.5g
AL value ≥78μH@1kHz/0.3V
P/N: CP25-40-10A
ID=25mm, OD=40mm, H=10mm (nominal), weight: 50.1g
Le: 10.21cm, Ac: 0.56cm2, CMC (common mode choke) core
AL value ≥27μH@16kHz/1V, high permeability and low iron loss
Excellent thin nanocrystalline ribbon with range from 0.018 to 0.025mm
Ribbon automatically wound in large-scale production, competitive price
P/N: CP32-40-15A
ID=32mm, OD=40mm, H=15mm (nominal)
Le:11.3cm, Ac: 0.45cm2, Weight: 52g
AL value ≥47.2μH@10kHz/0.1V/1Ts
15mm 1k107 ribbon wound, fixed by sponge after annealing
Adjustable remanence due to different annealing technical